Xometry offers a variety of processes that can manufacture parts in a rubbery material, both through 3D printing and tooled methods. Knowing which processes are available can help guide you to choose the right process for your part. A brief description of each process, material, advantages, and trade-offs of each process are outlined below.
HP MJF (TPU 88A)
HP Multi Jet Fusion builds parts from a powder bed by selectively applying agents and heating to create specific melts. This is repeated layer-by-layer, building a 3D printed part without the need for support structures. Rubber-like TPU (thermoplastic urethane) can be printed in this material, and it can even be vapor smoothed for an enhanced surface and properties.
- Process: HP Multi Jet Fusion (MJF)
- Material: TPU 88A
- Advantages: Quick lead times; great for test fits scalable production; relatively inexpensive compared to tooling; high accuracy; end-use durability; can be vapor smoothed
- Shore A Values: Shore A 88
- Disadvantages: Matte surface without vapor smoothing. Slightly looser tolerances than typical MJF materials.
GIF: HP MJF TPU 88A with vapor smoothing
Nexa3D LSPc (xFLEX)
Nexa3D's Lubricant Sublayer Photo-curing (LSPc®) technology provides extremely fast and accurate 3D printing, making it suitable for low volumes to production quantities. The "xFLEX" series of materials from Nexa3D are rubber-like elastomers with 150%-230% elongation to break and are a great alternative to urethane casting for higher quantities of smaller parts.
- Process: Nexa3D LSPc
- Materials:
- xFLEX402 (Shore A 73; 230% elongation at break)
- xFLEX475 Black (Shore A 44; 150% elongation at break)
- xFLEX475 White (Shore A 55; 159% elongation at break)
- Advantages: Quick lead times; great for scaling production of smaller parts; relatively inexpensive compared to casting; high accuracy; end-use durability
- Disadvantages: Higher upfront cost at very low quantities, supporting structure may have remanents
Carbon DLS (EPU and SIL)
Carbon DLS, known as Digital Light Synthesis, is an additive manufacturing method that forms isotropic features in a variety of engineered materials. Two DLS materials are rubber-like: EPU and SIL. Both have high durability and over 300% elongation to break, offering an alternative to traditional casting or molding of smaller rubber components.
- Process: Carbon DLS
- Material: EPU 40 (Shore A 68 Elastomeric Polyurethane) and SIL 30 (Shore A 35 Urethane Silicone)
- Advantages: Quick lead times; great for test fits scalable production; relatively inexpensive compared to tooling; high accuracy; end-use durability
- Shore A Values: EPU 40 comes in a black A68, SIL 30 comes in a gray A35
- Disadvantages: Higher upfront cost at very low quantities, supporting structure may have remanents
PolyJet 3D (rubber-like)
PJ3D is an additive manufacturing process where a printer head precisely deposits a UV-curable resin to construct parts from a 3D CAD file.
- Process: PJ3D
- Material: Rubber-like
- Advantages: Quick lead times; great for test fits and one-off prototypes; relatively inexpensive; incredible accuracy with tolerances as low as +/- 0.0035” or +/- 0.0005” per inch (+/- 0.013mm or +/- 0.09mm)
- Shore A Values: PolyJet can print in black Shore A 27, 40, 50, 60, 70, 85, and 95. Shore A values range from very soft on the lower numbers and more firm on the higher numbers.
- Disadvantages: Fragile for small features; tears easily (it does not stretch like rubber); removing support material may restrict freedom of design. Shore values may soften if in a humid or heated environment.
Video: Carbon DLS vs. Polyjet 3D printed rubber-like materials
Urethanes and Silicones
Urethane Casting consists of a two-part process of first 3D printing a master pattern to serve as a template for a silicone mold, which will then be used to cast parts.
- Process: Urethane Casting
- Material: Urethane; Silicone
- Advantages: End-use durability; abrasion and tear-resistant; color matching; different surface finish options; parts can be up to 30” (762mm) long
- Shore A Values: Most Shore A durometers can be easily met and matched for ultimate customization.
- Disadvantages: Longer lead times than 3D printing; more expensive due to upfront pattern and tooling costs
Thermoplastic Elastomers and Liquid Silicon Rubber
Injection molding consists of CNC machining a metal tool with cavities and using a press to inject melted material inside the cavity, forming the part. The tool then opens, and the part is released. Injection molding has the highest scalability of any of Xometry's processes due to low part cost but relatively higher upfront costs. Compression molding is available for elastomers as well, which uses a pre-measured "charge" of material placed into a mold cavity that compresses and forms the charge into the shape of the part.
- Process: Injection Molding / Compression Molding
- Material: TPE, TPV, PVC, LSR, EPDM, Customer Supplied, Custom Requests
- Advantages: End-use durability; abrasion and tear-resistant; color matching; different surface finish options; incredible scalability from 50 to beyond 50,000 units
- Shore A Values: Most Shore A durometers can be easily met and matched for ultimate customization.
- Disadvantages: Longer lead times than 3D printing; more expensive due to upfront setup and tooling costs but has cheaper per-part costs
Visit our main capability pages to learn more:
Visit our urethane casting services page